报道了一种利用激光二极管(LD)端面抽运Nd∶YVO4激光晶体, 通过硼酸铋(BIBO)晶体的腔内和频(SFM)与倍频(SHG), 实现3个二次谐波连续激光同时输出的3波长激光器。利用Nd∶YVO4晶体的两条发射谱线(分别为1064 nm和1084 nm)作为基频光, 并选择长度为1.5 mm, I 类临界相位匹配方式切割(对于1064 nm倍频)的BIBO作为非线性晶体, 通过调节BIBO晶体对3个非线性过程(1064 nm倍频, 1084 nm倍频及1064 nm与1084 nm和频)的相位因子, 即非线性过程的转换效率, 使激光器同时获得了两个倍频光和一个和频光, 即3个波长：532 nm, 537 nm和542 nm激光输出。实验结果表明当两个基频光波长相差较小时, 采用相位允许角小的非线性晶体同时进行腔内和频与倍频是获得多波长固体激光器的一种实用方法。

Calcium is one prospective element for the modern optical frequency standard. The 423-nm transition line of calcium atoms has been widely used in laser slowing and laser cooling, the precise spectrum measurement, and the magnetic optical trapping (MOT). However, there is no any available commercial diode laser working at this wavelength. We built a 423-nm laser based on extra bow-tie cavity and by using a Brewster-cut uncoated BIBO (BiB3O6) crystal, which worked at room temperature, with conversion efficiency of 3.75%, and a potential up to 20%.

利用自准直法，在30℃到170℃温度范围内分别测量0．4880 μm、0．6328 μm、1．0640 μm、1．3414 μm等波长下BiB₃O₆(BIBO)晶体的主轴折射率．得到不同温度下的Sellmeier方程及各主轴折射率的温度系数．计算了1．0795 μm下BIBO晶体的的主轴折射率．与实验测量的结果进行比较，两者的差异不大于2×10^－4．

BIBO(BiB3O6)晶体是一种新型的非线性光学晶体,物化性能稳定、光损伤阈值高,并且具有相当大的非线性光学系数,可以制作成频率变换器件,获得高效的倍频激光输出。报道了用BIBO晶体对一台运转于946 nm激光谱线的激光二极管(LD)抽运Nd:YAG激光器进行腔内倍频获得高效率的473 nm蓝光输出的实验结果。用国产的激光二极管端面抽运厚2.2 mm,掺杂浓度1.0 at.-%的Nd:YAG激光晶体,在注入抽运光功率为1.6 W时,用5 mm长的Ⅰ类临界位相匹配BIBO晶体获得的TEM00模蓝光输出达183 mW,相应的腔内倍频转换效率为11.4%,比同样工作条件下10 mm长Ⅰ类LBO晶体的倍频效率高45%以上。

采用高温溶液法成功生长出高光学质量的硼酸铋(BIBO)晶体,尺寸达到24 mm×19 mm×35 mm,质量为48 g。对BIBO晶体进行了定向,并测量了该晶体的主轴折射率。讨论了BIBO晶体的1064 nm三倍频性质,包括相位匹配角、有效非线性光学系数??d???? eff??、容限角、走离角等。结果表明,BIBO晶体的最佳三倍频方向为(137.7°,130°),其有效非线性光学系数值达到3.60 pm/V,属I类相位匹配。就主平面内的相位匹配方向而言,(146.4°,90°)具有最大的有效非线性光学系数值,为3.16 pm/V。在1064 nm的腔外三倍频实验中,(146.4°,90°)BIBO晶体的转换效率达到39.5 %,角度容限半宽为0.22 mrad?cm,该数值与0.175 mrad?cm的计算值基本符合。由于(33.6°,90°)BIBO晶体的有效非线性光学系数较小(0.31 pm/V),其三倍频转换效率小于5 %。