激光与光电子学进展, 2018, 55 (5): 053101, 网络出版: 2018-09-11
溶剂蒸发退火对银纳米线薄膜性能的增强 下载: 1562次
Enhancement of Properties of Silver Nanowire Films Through Solvent Evapor Annealing
图 & 表
图 2. AgNW薄膜的(a)方阻和品质因数及(b)透光率随甲醇溶剂蒸发退火处理时间的变化
Fig. 2. (a) Sheet resistance, quality factor, and (b) transmissivity of AgNW films at different solvent vapor annealing time
图 3. 经不同溶剂蒸发退火处理后的AgNW薄膜的方块电阻
Fig. 3. Sheet resistance of AgNW films after different solvent vapor annealing
图 5. AgNW溶剂蒸发退火(a)前和(b)后的TEM形貌
Fig. 5. TEM morphologies of AgNWs (a) before and (b) after solvent vapor annealing
图 6. AgNW溶剂蒸发退火(a)前和(b)后的接触电阻示意图
Fig. 6. Schematic of contact resistance of AgNWs (a) before and (b) after solvent vapor annealing
图 7. 以AgNW为阳极的聚合物太阳能电池的J-V曲线
Fig. 7. J-V curve of polymer solar cells with AgNW films as anodes
万慧军, 魏优, 钟远聪, 章勇. 溶剂蒸发退火对银纳米线薄膜性能的增强[J]. 激光与光电子学进展, 2018, 55(5): 053101. Huijun Wan, You Wei, Yuancong Zhong, Yong Zhang. Enhancement of Properties of Silver Nanowire Films Through Solvent Evapor Annealing[J]. Laser & Optoelectronics Progress, 2018, 55(5): 053101.