从HADS 产品像素漏光现象出发, 分析了HADS 产品产生像素漏光的主要原因和机理。通过分析发现, HADS 产品像素漏光主要是因为摩擦弱区液晶配向角度异常导致的透过率差异产生的。并在此基础提供摩擦方向优化和PS形状优化以减少摩擦弱区对像素漏光的影响。为更好画面品质的HADS产品提供了改善方向。

为了研究聚酰亚胺（PI）溶液黏度对TFT玻璃基板粘接性能的影响, 本实验制备了一系列不同黏度的PI溶液。通过制备5层粘接试样研究了PI液黏度大小对TFT基板粘接强度的影响。研究发现, 在PI液黏度从86 CP减小到15 CP过程中, 其和TFT基板的粘接强度呈现先增大后减小的趋势。这是因为当PI液黏度较大时, 粘接剂和被粘物表面的接触距离远和接触面积小是抑制粘接强度增大的关键因素, 而当PI液黏度较小时, PI膜本身的内聚能小则是阻碍粘接强度增大的关键因素。当PI液黏度为37 CP时, 能同时满足低黏度和高粘接强度的生产要求。

Laser beam far-field alignment as well as frequency-doubling and frequency-tripling crystal adjustment is very important for high-power laser facility. Separate systems for beam and crystal alignment are generally used while the proposed approach by off-axial grating sampling share common optics for these two functions, reducing both space and cost requirements. This detection system has been demonstrated on the National Laser Facility of Israel. The experimental results indicate that the average far-field alignment error is <5% of the spatial filter pinhole diameter, average autocollimation angle error of crystals is <10 μrad, and average frequency-tripling conversion efficiency is 69.3%, which meet the alignment system requirements on the beam direction and crystals.

为了制备具有自取向功能的聚酰亚胺(PI)取向膜, 避免摩擦工序在取向膜表面造成静电、灰尘、配向不良等不利影响, 本实验通过一系列黏度不同且有水平及垂直取向功能的PI溶液, 研究了PI液黏度和其取向膜表面粗糙度的关系, 进而研究了PI膜表面粗糙度和液晶预倾角(θp)的关系。研究发现: 取向膜表面粗糙度随着PI液黏度的增大而增大, θp随着粗糙度的增大而增大, 但当粗糙度大于一定值(3.760 nm)后, θp增长缓慢并趋于稳定。这主要是因为PI液黏度增大时, 阻碍了相邻PI液滴通过分子链段协同运动向彼此扩散的几率, 进而形成取向膜表面的“峰谷”形貌, 这种“峰谷”形貌表面对液晶垂直取向起到了支撑作用, 正是这种支撑作用使得液晶分子获得较大的θp。结合液晶面板响应时间对高预倾角的要求和Inkjet PI液滴喷嘴过小对PI液黏度的限制, 得出PI液黏度大约为41CP时, 此时取向膜表面粗糙度为4.830 nm, 液晶取向角为5.5°, 能较好地满足液晶取向的要求。

成功合成带有三苯胺和吡喃环结构的新型功能性二胺4-[(2-二氢吡喃)氧]-4’,4”－二氨基三苯胺 (THP)。使用此单体与4,4′-二氨基二苯醚 (ODA) 和4,4′-(六氟异丙烯)二酞酸酐 (6FDA) 共聚，利用两步化学酰胺化法，制备了共聚物的组成配比不同的3种聚酰亚胺 (PI)。使用NMR、FT-IR、DSC、UV-Vis等测试手段对单体和PI进行了结构表征和各项性能测试。研究了其溶解性能、耐热性能、透光性能和取向性能。结果表明3种PI均可溶于NMP、DMF等极性溶剂，同时在THF、DCM等低沸点溶剂中也具有较好的溶解性。 PI的玻璃化转变温度在270 ℃以上，在500~800 nm区域透过率在80 %以上，液晶分子的预倾角随THP的增加而增大，可达2.3°, 且具有均一的取向效果。

Laser beam far-field alignment as well as frequency-doubling and frequency-tripling crystal adjustment is very important for high-power laser facility. Separate systems for beam and crystal alignment are generally used while the proposed approach by off-axial grating sampling share common optics for these two functions, reducing both space and cost requirements. This detection system has been demonstrated on the National Laser Facility of Israel. The experimental results indicate that the average far-field alignment error is <5% of the spatial filter pinhole diameter, average autocollimation angle error of crystals is <10 μrad, and average frequency-tripling conversion efficiency is 69.3%, which meet the alignment system requirements on the beam direction and crystals.

在工业生产中，STN液晶取向剂在以薄膜形式涂覆在玻璃基板表面并进行热固化后，需要用溶剂对其进行洗涤。在洗涤中，薄膜从玻璃基板上脱落的现象时有发生。针对这种现象，需要一种添加剂，在不影响STN液晶取向剂的粘度、外观、预倾角、硬度等性质的同时，提高其粘接性能。在液晶取向剂中引入了N-苯基-3-氨基丙基三甲氧基硅烷(Y9669)添加剂，将硅烷添加剂以不同添加比例与取向剂搅拌混合后，得到5份添加剂含量不同的溶液。表征并对比了含有不同含量添加剂的STN液晶取向剂的粘度、外观、预倾角、硬度、粘接性等性质。实验结果表明：对于STN液晶取向剂体系，硅烷添加剂Y9669的最佳添加比例为取向剂固含量的0.5%，此时得到的取向剂综合性能更加优异。硅烷添加剂Y9669基本能够达到在不影响取向剂其他性能的同时，提高其对基板粘接性能的要求。

成功地合成了二胺单体十二烷氧基苯-4′,4″-二氨基三苯胺(DPDTA), 并用此单体与3,3′-二甲基-4,4′-二氨基二苯甲烷(DMMDA)和二苯醚四羧酸二酐(ODPA)共缩聚, 采用低温缩聚-热酰亚胺化、通过调节共聚物组成制备了2种聚酰亚胺(PI)。利用FT-IR、NMR、UV-Vis 与DSC 等手段对合成二胺单体及PI进行了结构表征和性能测试。研究了其取向性能、透光性能和耐热性能。结果表明, 在摩擦前, 含10% DPDTA的PI不能诱导液晶分子取向, 含25% DPDTA的PI能诱导液晶分子垂直取向, 预倾角可达89.6°。而摩擦后, 两种PI都能使液晶分子平行取向, 预倾角分别为1.8°和2.4°。两种PI膜在500~800 nm区域透光率都在80%以上, 玻璃化温度都在230 ℃以上。

介绍了一种新型纳米结构液晶取向膜技术，详述该取向膜的机理和最新进展。该取向膜本身是不均匀的，但不均匀性在亚微米以下，可以为液晶分子提供均匀的取向，并且产生任何在0~90°范围内的预倾角，具有良好的可靠性和可控性。分析了获得这样均匀取向性能的条件，提出3种产生纳米结构液晶取向膜的方法。

在惯性约束聚变（ICF）实验研究中，三次谐波转换单元是ICF驱动器重要的组成部分，为了缩短晶体的在线调试发次与时间，需先对单元进行离线调试。其基本原理是，通过扫描、测量倍频和三倍频晶体在不同倾斜角度下的谐波转换效率，然后利用多项式函数拟合数据，绘制谐波转换效率随倾斜角度变化的调谐曲线，确定最佳匹配位。基于理论分析，设计了一套高精度、自动化的三倍频离线调试系统。通过对现有系统的改进实验，以及对结果的分析表明，系统自动工作性能良好，单点测试的重复精度为±30 μrad，能量测量精度达到4%。