The pre-treatment of few-mode fibers (FMFs) has been successfully done with CO2 laser. The wavelength difference, Δ. between the two resonant wavelengths in the few-mode fiber Bragg grating (FMFBG) varies with temperature increment during the annealing process. The results show that the treated fibers with lower stresses have lower thermal sensitivity in Δ. than that of non-treated fiber. However, the treated fibers produce FMFBGs with better thermal durability and regeneration ratio. It is conceived that the presence of those stresses in the pristine fiber is responsible for the high thermal sensitivity in Δ.. The thermal relaxation of stresses and structural rearrangement during the thermal annealing process are responsible for the degradation of the strength and resilience of the regenerated grating.

为了研究6061-T6 铝合金激光喷丸后表面残余压应力在循环加载过程中的释放特性，对典型单联狗骨状试样进行激光喷丸处理及保温处理，利用MTS-809 拉扭组合材料测试系统进行不同循环应力水平和循环周次的疲劳实验，并使用X-350A 型X 射线应力测定仪测量试样表面残余压应力的变化。结果表明，残余压应力的松弛主要发生在疲劳过程开始的100 次循环周期内，1000 次循环周期后残余压应力基本趋于稳定。不同应力水平下的松弛行为表明，循环应力较小时，残余压应力松弛的幅度和速率相对较小；当循环应力接近材料屈服强度时，残余压应力松弛的幅度和速率较大，循环后期残余压应力完全释放，在表面产生残余拉应力。与未经保温处理的激光喷丸试样相比，试样经过150 ℃保温处理10 min 后，表面残余压应力下降，但在循环载荷作用下应力松弛的幅度和速率都较小，残余压应力的稳定性得以提升。

采用多光束应力实时测量装置监控并分析了磁控溅射Si和SiNx薄膜的总力及应力演化过程。在两种膜层中均观察到了应力释放及恢复现象。Si膜中应力是可逆的，而SiNx膜中应力是部分可逆的。物理吸附和解吸附分别是应力释放和恢复的主要原因。不可逆的应力分量来源于化学吸附，基于吸附机制建立了一个应力释放模型。

为了获得更好的微压印工艺填充效果,利用有限元方法研究模压工艺的主要参数压印温度、压印力和压印时间对压印效果的影响,并对工艺参数进行优化;对压印过程中不同的模具结构的应力分布进行了研究。仿真结果表明,工艺参数优化为480℃,30N,1800s后,模具的填充率达到97.2%;对不同的模具结构,有相同的应力分布区域,在模具拐角处会有应力的高度集中,与模具接触区域的应力相对较高,模具腔体区应力最低。

基于一维应力松弛模型和粘弹性本构关系,对1.06μm连续激光照射下K9玻璃板中的温升和应力作了计算,结果表明,由于应力松弛效应,激光停照后的冷却过程中产生的残余拉伸应力可达到玻璃的拉伸断裂强度阈值,而激光加热期间的最大压缩应力却小于压缩断裂强度要求.对3mm厚的K9玻璃板,由应力松弛引起破坏所要求的激光参数为946kWcm²作用0.2s,因而应力松弛可能为1.06μm连续激光大光斑照射下K9玻璃窗口损伤的主要模式.