无机材料学报, 2022, 37 (12): 1259, 网络出版: 2023-01-12 复制并引用该论文  被引通知

图 & 表

图 1. 三种涂层的XRD图谱

Fig. 1. XRD patterns of three kinds of coatings

下载图片 查看原文

图 2. 三种涂层的热膨胀曲线

Fig. 2. Thermal expansion curves of freestanding coatings

下载图片 查看原文

图 3. 不同温度下三种涂层的(a) 热导率和(b)3~5 μm单波段的红外发射率

Fig. 3. (a) Thermal conductivity and (b) single band (3-5 µm) infrared emissivity of freestanding coatings at different temperatures

下载图片 查看原文

图 4. 三种涂层的维氏硬度和断裂韧性

Fig. 4. Vickers hardness and fracture toughness of freestanding coatings

下载图片 查看原文

图 5. 热循环过程中涂层表面和金属基底的温度变化曲线

Fig. 5. Temperature changes of surface of coatings and metallic substrate during thermal cycling

下载图片 查看原文

图 6. 沉积态涂层截面和表面SEM照片

Fig. 6. SEM images of cross-sections and top surfaces of as-sprayed coatings

下载图片 查看原文

图 7. 热循环失效后三种涂层在不同位置的截面SEM照片及其元素分布图

Fig. 7. SEM images of cross-sections and elemental mappings of failed coatings at different positions

下载图片 查看原文

图 8. 三种涂层的热循环寿命

Fig. 8. Thermal cycle life times of three kinds of coatings

下载图片 查看原文

表 1主要实验用化学试剂

Table1. Chemical reagents for main experiments

Chemical reagent Purity Manufacturer La2O3 99.9% Beijing Chemical Works MgO 99.9% Jiangsu Hanos Chemical Co., LTD Al2O3 99.9% Shanghai Chemetall Chemicals Co., LTD ZnO 99.9% Hubei Longma Chemical Co., LTD CuO 99.9% Nanjing Xincai Chemical Co., LTD CaO 99.9% Nanjing Xincai Chemical Co., LTD Metallographic cold inlay — Wuxi Huazheng Metallurgical Technology Co., LTD Gumacabic powder AR Shanghai Sinopharm Group Chemical Reagent Co. LTD Ammonium citrate tribasic AR Beijing Chemical Works

查看原文

表 2等离子喷涂的参数

Table2. Parameters of APS

Item Bonding layer Ceramic layer Spraying distance/mm 100 100 Power/kW 42 42 Current/A 530 530 Plasma gas/SLPM 32/12 32/12 Migration rate/(mm·s−1) 1000 1000 Feed rate/(g·min−1) 30 35

查看原文

蔚海浪, 曹学强, 邓龙辉, 蒋佳宁. LaMeAl₁₁O₁₉/YSZ热障涂层热力学性能和热循环寿命[J]. 无机材料学报, 2022, 37(12): 1259. Hailang WEI, Xueqiang CAO, Longhui DENG, Jianing JIANG. Thermodynamic Properties and Thermal Cycling Lifetimes of LaMeAl₁₁O₁₉/YSZ Thermal Barrier Coatings[J]. Journal of Inorganic Materials, 2022, 37(12): 1259.