激光参数对硼磷合金铸铁缸套微坑形貌影响研究

采用Nd:YAG激光器对硼磷合金铸铁缸套试样进行激光微孔加工。研究了激光能量密度, 脉冲次数, 重复频率和聚焦条件等参数对微坑几何形貌的作用规律, 采用3D共聚焦显微镜及扫描电镜观察分析了微坑表面形貌和尺度随激光参数的变化。发现随着激光能量密度和脉冲次数的增加, 微坑的直径和深度均逐渐增大, 但增大幅度随能量密度增加而逐渐减小; 微坑直径随激光重复频率的增加而减小, 随着负离焦量的增加而增加; 微坑深度随负离焦量呈先增加后减小的趋势。对激光辐照硼磷合金铸铁的烧蚀阈值进行计算, 在单脉冲辐照条件下硼磷合金铸铁的烧蚀阈值为8.4 J/cm2, 脉冲次数对材料的烧蚀阈值产生累积效应, 烧蚀阈值随脉冲数量增加而减小, 累积系数为0.87。

Abstract

The surface treatment of the boron-phosphorus alloy cast iron cylinder liner sample was carried out on a Nd: YAG laser. The effects of laser parameters, such as energy density, pulse number, repetition frequency and focusing conditions, on the geometry of the micro-pits were studied through the surface morphology and scale of the micro-pits with 3D confocal microscopy and scanning electron microscopy. The diameter and depth of the micro-pits increase with the increase of laser energy density and the number of pulses, and the increase amplitude decreases with the increase of the energy density; the diameter of the micro-pits decreases with the increase of the laser repetition frequency, while the effect of the amount of negative defocus shows a reverse trend; The depth of the micro-pit increases first and then decreases with the amount of negative defocus. The ablation threshold of laser-irradiated boron-phosphorus alloy cast iron was calculated, the ablation threshold of boron-phosphorus alloy cast iron under single-pulse irradiation was 8.4 J/cm2, and the pulse number has an accumulation effect on ablation threshold, and the cumulative coefficient is 0.87.

参考文献

[1] 李敦桥, 刘小君, 黄毅, 等.规则凹坑表面的连通性分析［J］.合肥工业大学学报, 2009, 32 (11): 1633-1636.

[2] 金梅, 韩晓光, 沈岩, 等.微坑分布位置对复合润滑结构缸套摩擦磨损性能的影响规律［J］.中国表面工程, 2017, 30(6): 158-166.

[3] 万轶, 熊党生.激光表面织构化改善摩擦学性能的研究进展［J］.摩擦学学报, 2006, 26 (6): 603-607.

[4] 占剑, 杨明江.YAG激光微坑刻蚀分布对缸套-活塞环摩擦磨损性能影响［J］.内燃机学报, 2011, 29(1): 84-89.

[5] 华希俊, 葛汉青, 符永宏, 等.内燃机气缸内孔分区异化激光微织构技术研究［J］.内燃机工程, 2015, 36(4): 140-143.

[6] YANG J, ZHAO Y, ZHU X.Transition between nonthermal and thermal ablation of metallic targets under the strike of high-fluence ultrashort laser pulses［J］.Applied Physics Letters, 2006, 88(9): 094-101.

[7] TUNNA L, O’NEILL W, KHAN A, et al.Analysis of laser micro drilled holes through aluminium for micro-manufacturing applications［J］.Optics and Lasers in Engineering, 2005, 43(9): 937-950.

[8] SCHNEIDER M, BERTHE L, FABBRO R, et al.Study of hole properties in percussion regime with a new analysis method［J］.Journal of Physics D: Applied Physics, 2007, 2(2): 128-132.

[9] 刘勇, 冯爱新, 贾天代, 等.515 nm皮秒激光环切加工微孔实验研究［J］.应用激光, 2019, 39(2): 285-290.

[10] 符永宏, 刘强宪, 叶云霞, 等.同点间隔多次激光微织构工艺研究［J］.中国激光, 2015, 42 (12): 106-113.

[11] 苏永生, 李亮, 何宁.激光加工硬质合金刀具表面微织构的试验研究［J］.中国激光, 2014, 41(6): 66-72.

[12] 穆景阳, 万红, 白书欣.长脉冲激光辐照下环氧树脂的热烧蚀规律［J］.强激光与粒子束, 2008, 20(1): 36-40.

[13] NOSONOVSKY M, BHUSHAN B.Multiscale friction mechanisms and hierarchical surfaces in nano- and bio-tribology［J］.Materials Science & Engineering R, 2007, 58 (3-5): 162-193.

[14] 何江涛.飞秒激光加工的轴承钢表面微织构润滑减摩特性研究［D］.哈尔滨: 哈尔滨工业大学, 2017.

[15] BAUBEAU E, HARZIC R L, JONIN C, et al.Micromachining with high repetition rate femtosecond laser sources［C］//Proceedings of SPIE - The International Society for Optical Engineering, 2000, 4088: 48-50.

[16] 纪亮, 张晓兵, 张伟, 等.DD6镍基单晶合金的纳秒及皮秒激光烧蚀和制孔研究［J］.应用激光, 2014, 34(6): 551-556.

[17] 夏博, 姜澜, 王素梅, 等.飞秒激光微孔加工［J］.中国激光, 2013, 40(2): 6-17.

[18] BONSE J, BAUDACH S, KRGER J, et al.Femtosecond laser ablation of silicon-modification thresholds morphology［J］.Applied Physics A (Materials Science Processing), 2002, 74(1): 19-25.

郎平, 徐阳阳, 袁晓帅, 徐久军, 单英春, 韩晓光. 激光参数对硼磷合金铸铁缸套微坑形貌影响研究[J]. 应用激光, 2020, 40(3): 476. Lang Ping, Xu Yangyang, Yuan Xiaoshuai, Xu Jiujun, Shan Yingchun, Han Xiaoguang. Study on Influence of Laser Parameters on Micro-pit Morphology of Boron-Phosphorus Cast Iron Cylinder Liner[J]. APPLIED LASER, 2020, 40(3): 476.

激光参数对硼磷合金铸铁缸套微坑形貌影响研究

关于本站 Cookie 的使用提示

全站搜索

激光参数对硼磷合金铸铁缸套微坑形貌影响研究

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索