激光重熔等离子喷涂Al2O3—13% TiO2陶瓷涂层热震性能

王东生; 田宗军; 王泾文; 段宗银; 沈理达; 黄因慧

应用激光, 2010, 30 (4): 264, 网络出版: 2010-12-07

激光重熔等离子喷涂Al₂O₃—13% TiO₂陶瓷涂层热震性能

Thermal Shock Behavior of Laser Remelting Al₂O₃-13% TiO₂ Ceramic Coating Fabricated by Plasma Spraying

论文大纲

王东生 ^1,2田宗军 ²王泾文 ¹段宗银 ¹沈理达 ²黄因慧 ²

作者单位

¹ 铜陵学院机械工程系, 安徽铜陵 244000

² 南京航空航天大学机电学院, 江苏南京 210016

摘要

为了提高等离子喷涂Al2O3-13%TiO2(质量分数)陶瓷涂层的抗热震性能，采用激光重熔工艺对涂层进行处理，研究了激光重熔对等离子喷涂层热震性能的影响，并探讨了涂层的热震失效机理。结果表明：相对于等离子喷涂试样，激光重熔涂层有较好的抗热震性能。等离子喷涂陶瓷涂层的热震失效形式基本为边角剥落，而激光重熔陶瓷涂层热震失效形式既有边角剥落又有相当数量的中间区域局部剥落。激光重熔对涂层热震性能的影响主要表现为降低涂层的初始抗破坏能力、减缓涂层的裂纹扩展速率以及改变涂层的破坏模式。

Abstract

In order to improve the thermal shock resistance of Al2O3-13 %TiO2 (mass fraction) ceramic coating prepared by plasma spraying, laser remelting experiment was carried out and the influences of laser remelting on thermal shock behavior on the plasma-sprayed coating were researched. Meanwhile, the thermal shock failure mechanisms of the coatings were discussed. The results showed that as a result of thermal shock experiments at 850℃, the laser-remelted coating had better thermal shock resistance than the plasma-sprayed coating. The failure mechanism of the plasma-sprayed coating was corner spalling. In contract, the failure mechanism of the laser-remelted was mainly corner spalling, as well as local pelling. The effects of laser remelting on thermal shock behavior of the as-sprayed coating are mainly as follows., decrease the initial thermal shock resistance of the coating, slowdown the formation of crack in coating and change the coating＇s failure mode.

参考文献

[1] Beele W,Marijnissen G,Lieshout A V.The evolution of thermal barrier coatings-status and upcoming solutions for today's key issues[J].Surface ＆ Coatings Technology,1999,120-121:61-67

[2] Guo H B,Kuroda S,Murakami H.Segmented thermal barrier coatings produced by atmospheric plasma spraying hollow powders[J].Thin Solid Films,2006,506-507:136-139

[3] . 等离子喷涂-激光重熔陶瓷涂层存在问题及改进措施[J]. 材料科学与工艺, 2002, 10(4): 431-435.

[4] . Thermal shock behavior of nanostructured and conventional A12O3/13wt%TiO2 coatings fabricated by plasma spraying[J]. Surface and Coatings Technology, 2007, 201(18): 7746-7754.

[5] . Thermal shock properties and failure mechanism of plasma sprayed A12O3/TiO2 nanocomposite coatings[J]. Ceramics International, 2005, 31: 817-824.

[6] . 等离子喷涂ZrO2/NiCoCrAIY梯度热障涂层的抗热震性及失效机理[J]. 材料热处理学报, 2001, 22(4): 21-24.

[7] . Fracture toughness,strength and thermal shock behaviour of bulk plasma sprayed alumina-effects of heat treatment[J]. Journal of the European Ceramic Society, 2000, 20: 1439-1452.

[8] . The resistance to wear and corrosion of laser-cladding Al2O3 ceramic coating on Mg alloy[J]. Applied Surface Science, 2007, 253(12): 5306-5311.

[9] . A study of wear resistance of plasma-sprayed and laser-remelted coatings on aluminium alloy[J]. Surface and Coatings Technology, 2000, 127: 233-238.

[10] Yang Y Z,Zhu Y L,Liu Z Y,et al.Laser remelting of plasma sprayed A12O3 ceramic coatings and subsequent wear resistance[J].Materials Science and Engineering A,2000,291(1-2):168-172

[11] . TiAl合金表面激光重熔Al2O3-13wt%TiO2复合陶瓷涂层组织结构[J]. 航空材料学报, 2008, 28(6): 51-56.

[12] . Fracture in single-layer zirconia (YSZ)-bond coat alloy(NiCoCrAlY)composite coatings under thermal shock[J]. Acta Materialia, 2004, 52(2): 455-465.

[13] . 氧化锆纳米等离子涂层的结构与热震性能研究[J]. 无机材料学报, 2006, 21(1): 250-256.

[14] Mesrati N,Saif Q,Treheux D,et al.Characterization of thermal fatigue damage of thermal barrier produced by atmospheric plasma spraying[J].Surface & Coatings Technology,2004,187(2-3):185-193

[15] . Thermal cyclic behavior of air plasma sprayed thermal barrier coatings sprayed on stainless steel substrates[J]. Surface & Coatings Technology, 2007, 201(8): 4653-4658.

[16] . TiAl合金表面激光重熔热障涂层组织及抗高温氧化性能[J]. 功能材料, 2009, 40(4): 578-581.

[17] Lee J H,Tsai P C,Chang C L.Microstructure and thermal cyclic performance of laser-glazed plasma-sprayed ceria-yttria-stabilized zirconia thermal barrier coatings[J].Surface ＆ Coatings Technology,2008,202(22-23):5607-5612

[18] . 激光-等离子束复合制备热障涂层高温性能试验研究[J]. 材料工程, 2003, 2: 19-22.

[19] . Laser surface remelting of plasma sprayed nanostructured Al2O3-13wt%TiO2 coatings on titanium alloy[J]. Applied Surface Science, 2009, 255(20): 8603-8610.

[20] 王东生,田宗军,沈理达,等.激光表面熔覆制备纳米结构涂层的研究进展[J].中国激光,2008,35(11):1698-1709.

王东生, 田宗军, 王泾文, 段宗银, 沈理达, 黄因慧. 激光重熔等离子喷涂Al₂O₃—13% TiO₂陶瓷涂层热震性能[J]. 应用激光, 2010, 30(4): 264. Wang Dongsheng, Tian Zongjun, Wang Jingwen, Duan Zongyin, Shen Lida, Huang Yinhui. Thermal Shock Behavior of Laser Remelting Al₂O₃-13% TiO₂ Ceramic Coating Fabricated by Plasma Spraying[J]. APPLIED LASER, 2010, 30(4): 264.

激光重熔等离子喷涂Al₂O₃—13% TiO₂陶瓷涂层热震性能

关于本站 Cookie 的使用提示

全站搜索