光催化被广泛用于去除水中的难降解有机污染物, 但是由于光生电子和空穴的复合率高, 抑制了半导体光催化剂的催化活性。本研究通过简便的溶剂热法成功制备了一种BiOBr/ZnMoO₄复合材料。通过结构分析、原位XPS、功函数测试、自由基捕获及电子顺磁共振(ESR)实验等证实了BiOBr/ZnMoO₄复合材料形成了S型异质结。实验结果表明, 适当ZnMoO₄含量的BiOBr/ZnMoO₄异质结可以显著提高BiOBr的光催化性能。与纯BiOBr、ZnMoO₄相比, 质量分数15% BiOBr/ZnMoO₄在可见光下表现出最佳的光催化活性, 双酚A的光催化降解率达到85.3% (90 min), 环丙沙星的光降解速率常数分别是BiOBr的2.6倍和ZnMoO₄的484倍。这可归因于BiOBr和ZnMoO₄之间形成了紧密的界面结合和S型异质结, 使得光生载流子可以实现有效的空间分离和转移。这项工作为定向合成Bi基S型异质结复合光催化材料提供了一种简便有效的方法, 对进一步理解Bi基多元异质结光催化材料的构效关系提供了新的理论和实验基础。

Photocatalysis is widely used for the removal of refractory organic pollutants in water, but the catalytic activity of semiconductor photocatalysts is significantly inhibited due to the high recombination rate of photogenerated electrons and holes. In this study, an S-scheme BiOBr/ZnMoO₄ composite was successfully prepared by a facile solvothermal method. The structure analysis, in-situ XPS, work function test, free radical capture and ESR experiment confirmed that the BiOBr/ZnMoO₄ composite formed an S-scheme heterojunction. The experimental results show that BiOBr/ZnMoO₄ heterojunction with appropriate ZnMoO₄ content can significantly improve the photocatalytic performance of BiOBr. Compared with pure BiOBr and ZnMoO₄, 15% BiOBr/ZnMoO₄ exhibits the best photocatalytic activity under visible light irradiation, and the photocatalytic degradation rate of bisphenol A reaches 85.3% (90 min). The rate constants of photodegradation of ciprofloxacin are 2.6 times that of BiOBr and 484 times that of ZnMoO₄, respectively. This can be attributed to the tight interfacial bonding between BiOBr and ZnMoO₄ and the formation of S-scheme heterojunction, which enables the efficient spatial separation and transfer of photogenerated carriers. This work provides a simple and efficient method for the directional synthesis of Bi-based S-scheme heterojunction photocatalytic materials, and provides a new theory and experimental basis for further understanding of the structure-activity relationship of Bi-based multi-heterojunction photocatalytic materials.