摘要

高收缩率是限制高性能工程水泥基复合材料(HP-ECC)大规模工程应用的瓶颈之一。本文通过引入超吸水性聚合物(SAP)来缓解HP-ECC的收缩, 研究了不同掺量的SAP对HP-ECC抗压强度、抗折强度、拉伸性能、自收缩和干燥收缩性能的影响, 并采用扫描电子显微镜(SEM)研究了SAP对HP-ECC拉伸后纤维表面形貌变化的影响。结果表明, HP-ECC中掺入SAP后的抗压强度和抗折强度降低, 自收缩和干燥收缩得到缓解, 且自收缩和干燥收缩随SAP掺量的增加而降低。此外, HP-ECC的拉伸强度降低, 拉伸延伸率提高。SAP的引入降低了基体的断裂韧度, 使基体更容易形成微裂缝, 从而改善了HP-ECC的应变硬化行为和多缝开裂现象。随着SAP掺量的增加, 纤维从基体中拔出时的表面形貌越来越光滑, 纤维-基体界面黏结性能降低。

Abstract

High shrinkage is one of the bottlenecks limiting the large-scale engineering application of high performance engineered cementitious composites (HP-ECC). This work alleviated the shrinkage of HP-ECC by introducing superabsorbent polymers (SAP). The effects of different amounts of SAP on the compressive strengthflexural strengthtensile propertiesautogenous shrinkage and dry shrinkage properties of HP-ECC were investigated. Scanning electron microscopy (SEM) was used to observe the changes in fiber surface morphology after stretching of HP-ECC caused by SAP. The results show that the addition of SAP reduces the compressive strength and flexural strength of HP-ECC and alleviates autogenous shrinkage and dry shrinkageand the autogenous shrinkage and dry shrinkage decreases with the increase of SAP content. MoreoverSAP reduces the tensile strength of HP-ECC and increases the tensile strain of HP-ECC. The incorporation of SAP reduces the fracture toughness of the matrixmaking it more prone to microcracksthereby improving the strain hardening behavior and multiple cracking of HP-ECC. It is observed that with the increase of SAP contentthe surface morphology of the fibers as they are pulled out of the matrix becomes smootherindicating a decreasing in fiber matrix interface adhesion.

参考文献

[1] DING YYU K QYU J Tet al. Structural behaviors of ultra-high performance engineered cementitious composites (UHP-ECC) beams subjected to bending-experimental study［J］. Construction and Building Materials2018177: 102-115.

[2] LI V C. On engineered cementitious composites (ECC). A review of the material and its applications［J］. Journal of Advanced Concrete Technology20031(3): 215-230.

[3] LI L ZCAI Z WYU K Qet al. Performance-based design of all-grade strain hardening cementitious composites with compressive strengths from 40 MPa to 120 MPa［J］. Cement and Concrete Composites201997: 202-217.

[4] ZHU J XXU L YHUANG B Tet al. Recent developments in engineered/strain-hardening cementitious composites (ECC/SHCC) with high and ultra-high strength［J］. Construction and Building Materials2022342: 127956.

[5] WU L MFARZADNIA NSHI C Jet al. Autogenous shrinkage of high performance concrete: a review［J］. Construction and Building Materials2017149: 62-75.

[6] LURA PJENSEN O MVAN BREUGEL K. Autogenous shrinkage in high-performance cement paste: an evaluation of basic mechanisms［J］. Cement and Concrete Research200333(2): 223-232.

[7] XUAN M YWANG Y SWANG X Yet al. Effect of cement types and superabsorbent polymers on the properties of sustainable ultra-high-performance paste［J］. Materials202114(6): 1497.

[8] JUSTS JWYRZYKOWSKI MBAJARE Det al. Internal curing by superabsorbent polymers in ultra-high performance concrete［J］. Cement and Concrete Research201576: 82-90.

[9] MECHTCHERINE VWYRZYKOWSKI MSCHRFL Cet al. Application of super absorbent polymers (SAP) in concrete construction: update of RILEM state-of-the-art report［J］. Materials and Structures202154(2): 80.

[10] YAO YZHU YYANG Y Z. Incorporation superabsorbent polymer (SAP) particles as controlling pre-existing flaws to improve the performance of engineered cementitious composites (ECC)［J］. Construction and Building Materials201228(1): 139-145.

[11] KHAN M IFARES G. Effect of temperature on strain capacity and cracking system of SHCC of different workability and SAP contents［J］. Construction and Building Materials2019213: 337-347.

[12] ZHANG M HZHU X ZLIU B Jet al. Mechanical property and durability of engineered cementitious composites (ECC) with nano-material and superabsorbent polymers［J］. Powder Technology2022409: 117839.

[13] 刘剑辉. SAP与FLWA在超高性能混凝土中的内养护作用［D］. 长沙: 湖南大学2019.

[14] SOLIMAN A MNEHDI M L. Effect of partially hydrated cementitious materials and superabsorbent polymer on early-age shrinkage of UHPC［J］. Construction and Building Materials201341: 270-275.

姜爱国, 杨维斌, 蔡杰. SAP对高性能工程水泥基复合材料性能的影响[J]. 硅酸盐通报, 2023, 42(11): 3836. JIANG Aiguo, YANG Weibin, CAI Jie. Effect of SAP on Properties of High Performance Engineered Cementitious Composites[J]. Bulletin of the Chinese Ceramic Society, 2023, 42(11): 3836.

SAP对高性能工程水泥基复合材料性能的影响

关于本站 Cookie 的使用提示

全站搜索

SAP对高性能工程水泥基复合材料性能的影响

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索