Effect of Annealing Temperature on Performance of Amorphous InWO Thin Film Transistors

论文大纲

许玲吴崎董承远

作者单位

上海交通大学电子工程系，上海 200240

非晶铟钨氧薄膜晶体管退火温度氧空位表面粗糙度 amorphous indium tungsten oxide thin film transistors annealing temperature oxygen vacancies roughness

摘要

非晶铟钨氧(a-IWO)薄膜晶体管(TFT)具有高迁移率和高稳定性的优点，但其适合于实际生产的制备工艺条件尚有待摸索。本文研究了退火温度对a-IWO TFT电学特性影响的基本规律和内部机理。实验结果表明，随着退火温度的升高，a-IWO TFT的场效应迁移率也相应增加，这是由于高温退火下a-IWO薄膜中氧空位含量增多并进而导致载流子浓度增加的缘故。此外，a-IWO TFT的亚阈值摆幅和阈值电压在200 ℃下退火达到最佳，我们认为主要原因在于此时a-IWO薄膜的表面粗糙度最小并形成了最佳的前沟道界面状态。

Abstract

Amorphous indium tungsten oxide (a-IWO) thin film transistors (TFTs) show superior electrical performance and stable properties, but their industrial fabrication methods still need to be developed. In this study, the effect of annealing temperature on the electrical performance of a-IWO TFTs was investigated, where the related basic dependence and physical essence were involved. The experimental results indicate that the field-effect mobility of a-IWO TFTs increases gradually with the annealing temperature increasing, due to the more oxygen vacancies as well as the larger carrier concentration at higher annealing temperatures. Meanwhile, annealing at 200 ℃ led to the best subthreshold swing and threshold voltage of a-IWO TFTs, as is assumed to mainly result from the best front-channel interface caused by the smallest roughness of the a-IWO films annealed at 200 ℃.

参考文献

[1] NOMURA K, OHTA H, TAKAGI A, et al.. Room-temperature fabrication of transparent flexible thin-film transistors using amorphous oxide semiconductors ［J］. Nature, 2004, 432(7016):488-492.

[2] LEE G J, KIM J, KIM J H, et al.. High performance, transparent a-IGZO TFTs on a flexible thin glass substrate ［J］. Semicond. Sci. Technol., 2014, 29(3):035003.

[3] HSU H H, CHANG C Y, CHENG C H. A flexible IGZO thin-film transistor with stacked TiO2-based dielectrics fabricated at room temperature ［J］. IEEE Electron. Dev. Lett., 2013, 34(6):768-770.

[4] MNZENRIEDER N, ZYSSET C, PETTI L, et al.. Flexible double gate a-IGZO TFT fabricated on free standing polyimide foil ［J］. Solid State Electron., 2013, 84:198-204.

[5] 苟昌华,武明珠,郭永林,等. 未退火InGaZnO作为缓冲层的InGaZnO薄膜晶体管性能研究［J］. 液晶与显示, 2015, 30(4):602-607.

GOU C H, WU M Z, GUO Y L, et al.. Effects of using InGaZnO without annealing as buffer layer on the performance of InGaZnO thin film transistors ［J］. Chin. J. Liq. Cryt. Disp., 2015, 30(4):602-607. (in Chinese)

[6] LIU G X, LIU A, ZHU H H, et al.. Low-temperature, nontoxic water-induced metal-oxide thin films and their application in thin-film transistors ［J］. Adv. Funct. Mater., 2015, 25(17):2564-2572.

[7] DOMINGUEZ M A, FLORES F, LUNA A, et al.. Impact of active layer thickness in thin-film transistors based on zinc oxide by ultrasonic spray pyrolysis ［J］. Solid State Electron., 2015, 109:33-36.

[8] LI H U, JACKSON T N. Oxide semiconductor thin film transistors on thin solution-cast flexible substrates ［J］. IEEE Electr. Device Lett., 2015, 36(1):35-37.

[9] LAN L F, XIONG N N, XIAO P, et al.. Enhancement of bias and illumination stability in thin-film transistors by doping InZnO with wide-band-gap Ta2O5 ［J］. Appl. Phys. Lett., 2013, 102(24):242102.

[10] AIKAWA S, DARMAWAN P, YANAGISAWA K, et al.. Thin-film transistors fabricated by low-temperature process based on Ga- and Zn-free amorphous oxide semiconductor ［J］. Appl. Phys. Lett., 2013, 102(10):102101.

[11] KIZU T, AIKAWA S, MITOMA N, et al.. Low-temperature processable amorphous In-W-O thin-film transistors with high mobility and stability ［J］. Appl. Phys. Lett., 2014, 104(15):152103.

[12] SHI J F, DONG C Y, DAI W J, et al.. The influence of RF power on the electrical properties of sputtered amorphous In-Ga-Zn-O thin films and devices ［J］. J. Semicond., 2013, 34(8):084003.

[13] ABE Y, ISHIYAMA N, KUNO H, et al.. Amorphous indium tungsten oxide films prepared by DC magnetron sputtering ［J］. J. Mater. Sci., 2005, 40(7):1611-1614.

[14] FUH C S, SZE S M, LIU P T, et al.. Role of environmental and annealing conditions on the passivation-free in-Ga-Zn-O TFT ［J］. Thin Solid Films, 2011, 520(5):1489-1494.

[15] RAJA J, JANG K, NGUYEN H H, et al.. Enhancement of electrical stability of a-IGZO TFTs by improving the surface morphology and packing density of active channel ［J］. Curr. Appl. Phys., 2013, 13(1):246-251.

许玲, 吴崎, 董承远. 退火温度对非晶铟钨氧薄膜晶体管特性的影响[J]. 发光学报, 2016, 37(4): 457. XU Ling, WU Qi, DONG Cheng-yuan. Effect of Annealing Temperature on Performance of Amorphous InWO Thin Film Transistors[J]. Chinese Journal of Luminescence, 2016, 37(4): 457.

退火温度对非晶铟钨氧薄膜晶体管特性的影响

关于本站 Cookie 的使用提示

全站搜索

退火温度对非晶铟钨氧薄膜晶体管特性的影响

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索