衬底温度对ITO薄膜及黑硅SIS型太阳电池性能影响

金磊; 李玉芳; 沈鸿烈; 唐群涛; 蒋晔; 郑超凡; 杨楠楠; 王洪美

doi:doi:10.3788/gzxb20174611.1116002

光子学报, 2017, 46 (11): 1116002, 网络出版: 2017-12-08

衬底温度对ITO薄膜及黑硅SIS型太阳电池性能影响

Effect of Substrate Temperature on the Properties of ITO Film and Black Silicon SIS Solar Cells

论文大纲

金磊 ^*李玉芳沈鸿烈唐群涛蒋晔郑超凡杨楠楠王洪美

作者单位

南京航空航天大学材料科学与技术学院, 江苏省能量转换材料与技术重点实验室, 南京 210016

摘要

结合反应离子刻蚀法和掩膜法在n型硅片表面制备出圆锥状结构黑硅, 利用湿法氧化法在硅片表面氧化出一层超薄SiOx, 采用磁控溅射法在其表面沉积一层掺锡氧化铟(IndiumTinOxide, ITO)薄膜, 在黑硅衬底上制备出ITO/SiOx/n-Si太阳电池。通过硅片表面纳米结构, 增加光吸收, 进而提高电池转化效率。研究结果表明, 在不同衬底温度下沉积ITO时, 薄膜都呈现出了良好的光学和电学性能.250 ℃时, ITO薄膜性能最优, 在400~1 000 nm波长范围内, 平均透过率达到93.1%, 并展现出优异的电学性能.通过优化H2O2预处理时间, 减小了SiOx层中氧空位缺陷, SIS电池短路电流得到明显提高, 从未处理前的26.84 mA/cm2提升到经H2O2处理15 min后的34.31 mA/cm2.此时, 电池性能最优, 转化效率达到3.61%.

Abstract

The cone nanostructures on n-silicon were fabricated by combination mask with reactive ion etching. After forming ultra-thin SiO2 on black silicon by wet oxidation method, the Indium Tin Oxide (ITO) film was deposited by magnetron sputtering equipment. Finally, the ITO/SiOx/n-Si solar cell was fabricated. The photoelectric conversion efficiency of cells improved because of nanostructures, which can increase the absorption of light. Results showed that ITO deposited at different temperatures and presented the good optical and electrical properties. The ITO film grown at 250 ℃ exhibited the excellent optical and electrical properties. In 400~1 000 nm wavelength, the average transmittance of ITO up to 93.1%. By optimizing the H2O2 pretreatment time, the short circuit current of SIS solar cell increased from 26.84 mA/cm2 to 34.31 mA/cm2 due to the oxygen vacancy defects decrease in SiOx layers. When using H2O2 pretreated black silicon for 15 min and deposited ITO at 150 ℃, the SIS solar cell conversion efficiency reached 3.61%.

参考文献

[1] HAUG H, OLIBET S, RNULF N, et al. Modulating the field-effect passivation at the SiO2/c-Si interface: Analysis and verification of the photoluminescence imaging under applied bias method［J］. Journal of Applied Physics, 2013, 114(17): 174502.

[2] GASTROW G V, ALCUBILLA R, ORTEGA P, et al. Analysis of the atomic layer deposited Al2O3 field-effect passivation in black silicon［J］. Solar Energy Materials & Solar Cells, 2015, 142: 29-33.

[3] SCHULZE T F, KORTE L, RECH B. Impact of a-Si: H hydrogen depth profiles on passivation properties in a-Si:H/c-Si heterojunction［J］. Thin Solid Films, 2012, 520(13): 4439-4444.

[4] SINGH R, GREEN M A, RAJKANAN K. Review of conductor-insulator-semiconductor (CIS) solar cells［J］. Solar Cells, 1981, 3(2): 95-148.

[5] KAJIYAMA K, FUUKAWA Y. Electrical and optical properties of SnO2-Si heterojunctions［J］. Japanese Journal of Applied Physics, 1967, 6(7): 905-906.

[6] GHOSH A K, FISHMAN C, FENG T. SnO2/Si solar cells-Heterostructure of Schottky-barrier or MIS-type device［J］. Journal of Applied Physics, 1978, 49(6): 3490-3498.

[7] SHEWCHUN J, DUBOW J, WILMSEN C W, et al. The operation of the semiconductor-insulator-semiconductor solar cell: Experiment［J］. Journal of Applied Physics, 1979, 50(4): 2832-2839.

[8] KOBAYASHI H, ISHIDA T, NAKATO Y, et al. Mechanism of carrier transport in highly efficient solar cells having indium tin oxide/Si junctions［J］. Journal of Applied Physics, 1991, 69(3): 1736-1743.

[9] MALIK O, HIDALGA W, ZUNIGA C, et al. Efficient ITO-Si solar cells and power modules fabricated with a low temperature technology: Results and perspectives［J］. Journal of Non-Crystalline Solids, 2008, 354(19-25): 2472-2477.

[10] FANG H W, HSIEH T E, JUANG J Y.Influences of SiOx layer thickness on the characteristics of In-Zn-O/SiOx/n-Si hetero-junction structure solar cells［J］. Surface & Coatings Technology, 2013, 231(9): 214-218.

[11] FANG H W, HSIEH T E, JUANG J Y. Effects of indium concentration on the efficiency of amorphous In-Zn-O/SiOx/n-Si hetero-junction solar cells［J］. Solar Energy Materials & Solar Cells, 2014, 121(2): 176-181.

[12] CHEN S M, GAO M, FANG X H, et al. Modifications and multiple roles of graphene film in SIS structural solar cells［J］. Solar Energy, 2015, 122: 658-666.

[13] 豆维江, 秦应雄, 巨小宝, 等. 多晶硅片反应离子刻蚀制绒后扩散工艺的匹配性［J］. 光子学报, 2013, 42(6):649-653.

DOU Wei-jiang, QIN Ying-xiong, JU Xiao-bao, et al. Diffusion processing and its matching property of multicrystalline silicon solar cells through reactive ion etching texturing［J］. Acta Photonica Sinica, 2013, 42(6): 649-653.

[14] 郑超凡, 沈鸿烈, 蒲天, 等. 银铜双原子MACE法可控制备倒金字塔多晶黑硅的结构与性能［J］. 光子学报, 2017, 46(1):0116002.

ZHENG Chao-fan, SHEN Hong-lie, PU Tian, et al. Structures and properties of black multicrystalline silicon with a structure of invert pyramid prepared controllably by Ag and Cu dually assisted chemical etching method［J］. Acta Photonica Sinica, 2017, 46(1): 0116002.

[15] HAMBERG I, GRANQVIST C G. Optical properties of transparent and heat-reflecting indium-tin-oxide films: Experimental data and theoreticalanalysis［J］. Solar Energy Material, 1984, 11(3): 239-248.

[16] VENKATACHALAM S, NANJO H, KAWASAKI K, et al. Preparation and characterization of nanocrystalline ITO thin films on glass and clay substrates by ion-beam sputter deposition method［J］. Applied Surface Science, 2011, 257(21): 8923-8928.

金磊, 李玉芳, 沈鸿烈, 唐群涛, 蒋晔, 郑超凡, 杨楠楠, 王洪美. 衬底温度对ITO薄膜及黑硅SIS型太阳电池性能影响[J]. 光子学报, 2017, 46(11): 1116002. JIN Lei, LI Yu-fang, SHEN Hong-lie, TANG Qun-tao, JIANG Ye, ZHENG Chao-fan, YANG Nan-nan, WANG Hong-mei. Effect of Substrate Temperature on the Properties of ITO Film and Black Silicon SIS Solar Cells[J]. ACTA PHOTONICA SINICA, 2017, 46(11): 1116002.

衬底温度对ITO薄膜及黑硅SIS型太阳电池性能影响

关于本站 Cookie 的使用提示

全站搜索

衬底温度对ITO薄膜及黑硅SIS型太阳电池性能影响

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索