粉煤灰掺量对海水海砂高性能混凝土性能的影响

张腾腾; 王传林; 张宇轩; 刘泽平

硅酸盐通报, 2022, 41 (5): 1677, 网络出版: 2022-07-21

粉煤灰掺量对海水海砂高性能混凝土性能的影响

Effect of Fly Ash Content on Performance of High Performance Concrete with Seawater and Sea Sand

论文大纲

张腾腾 ^1,*王传林 ^1,2张宇轩 ¹刘泽平 ¹

作者单位

¹ 汕头大学土木与环境工程系, 汕头 515063

² 汕头大学广东省结构安全与监测工程技术研究中心, 汕头 515063

摘要

通过宏观力学性能、化学收缩、pH值、氯离子浓度等测试和SEM、XRD等微观表征研究粉煤灰掺量对海水海砂高性能混凝土性能的影响。结果表明: 为维系钢筋钝化膜稳定, 高温蒸养时粉煤灰掺量不宜大于30%(质量分数, 下同), 标养时粉煤灰掺量不宜大于50%; 海水海砂高性能混凝土中游离Cl-浓度随养护时间波动, 前期先升高后骤降, 后期缓慢增加, 标养条件下Cl-浓度明显低于高温蒸养条件下; 海水海砂高性能混凝土具有早强性, 其强度随粉煤灰掺量增加大致呈下降趋势, 高温蒸养可明显提高混凝土抗折、抗压强度; 粉煤灰掺量越多, 残留的未水化颗粒越多, 高温蒸养可有效改善混凝土微观结构, 提高致密性; 粉煤灰掺量过多或过少均会增加硅酸盐水泥体系的化学收缩, 粉煤灰掺量为30%和40%时混凝土化学收缩值较小。

Abstract

The effect of fly ash content on the performance of seawater and sea sand high performance concrete was studied by carrying out experiments on mechanical properties, chemical shrinkage, pH value, chloride ion concentration, and microstructure. The results show that in order to maintain the stability of reinforcement passive film, the content of fly ash should not be greater than 30% (mass fraction, the same below) under high temperature steam curing and 50% under standard curing. The concentration of free Cl- in seawater and sea sand high performance concrete fluctuates with curing time, increases first and then decreases sharply in the early stage, and increases slowly in the later stage. The Cl- concentration under standard curing is significantly lower than that under high temperature steam curing. Seawater and sea sand high performance concrete has early strength, and its strength decreases with the increase of fly ash content. High temperature steam curing significantly improves the flexural and compressive strength of concrete. The more fly ash is added, the more unhydrated particles remain. High temperature steam curing effectively improves the microstructure and compactness of concrete. When fly ash content is too large or too small, it increases the chemical shrinkage of Portland cement. The chemical shrinkage value of concrete is small when the fly ash content is 30% and 40%.

参考文献

[1] 陈宗平,王心月,陈宇良,等.海砂海水混凝土力学性能试验研究［J］.混凝土,2020(11):1-7.

[2] 卢予奇,赵羽习.海砂颗粒形态评价与海拌混凝土性能研究［J］.海洋工程,2020,38(6):124-130.

[3] HASDEMIR S, TUGˇRUL A, YILMAZ M. The effect of natural sand composition on concrete strength［J］. Construction and Building Materials, 2016, 112: 940-948.

[4] 李薛忠.基于钢筋锈蚀的海工混凝土结构耐久性能研究［D］.镇江:江苏科技大学,2019.

[5] 王小刚,史才军,何富强,等.氯离子结合及其对水泥基材料微观结构的影响［J］.硅酸盐学报,2013,41(2):187-198.

[6] ZIBARA H, HOOTON R D, THOMAS M D A, et al. Influence of the C/S and C/A ratios of hydration products on the chloride ion binding capacity of lime-SF and lime-MK mixtures［J］. Cement and Concrete Research, 2008, 38(3): 422-426.

[7] ELAKNESWARAN Y, NAWA T, KURUMISAWA K. Electrokinetic potential of hydrated cement in relation to adsorption of chlorides［J］. Cement and Concrete Research, 2009, 39(4): 340-344.

[8] SURYAVANSHI A K, SCANTLEBURY J D, LYON S B. The binding of chloride ions by sulphate resistant Portland cement［J］. Cement and Concrete Research, 1995, 25(3): 581-592.

[9] 王绍东,黄煜镔,王智.水泥组分对混凝土固化氯离子能力的影响［J］.硅酸盐学报,2000,28(6):570-574.

[10] BEN-YAIR M. The effect of chlorides on concrete in hot and arid regions［J］. Cement and Concrete Research, 1974, 4(3): 405-416.

[11] 李师财,于泳,金祖权.海水海砂混凝土力学性能与耐久性研究综述［J］.硅酸盐通报,2020,39(12):3743-3752.

[12] SHI X M, YANG Z X, LIU Y J, et al. Strength and corrosion properties of Portland cement mortar and concrete with mineral admixtures［J］. Construction and Building Materials, 2011, 25(8): 3245-3256.

[13] 刘军,董必钦,邢锋,等.海砂氯离子与水泥胶体结合的模拟实验与结合机理［J］.硅酸盐学报,2009,37(5):862-866+876.

[14] 刘军,邢锋,董必钦,等.海砂型氯离子在混凝土中扩散的微观形貌分析［J］.混凝土与水泥制品,2007(6):15-17.

[15] 邢锋,刘军,董必钦,等.海砂型氯离子与水泥胶体的结合和机理［J］.东南大学学报(自然科学版),2006,36(s2):167-172.

[16] 刘军,邢锋,董必钦,等.模拟海砂混凝土中氯离子扩散研究［J］.混凝土,2008(3):33-35.

[17] 柳俊哲,蒋义,贺智敏,等.海砂混凝土中氯离子固化的影响因素研究［J］.材料导报,2013,27(20):129-132.

[18] 汪家昆,吴相豪,李志卫,等.粉煤灰影响海水海洋骨料水泥基材料抗压强度试验研究［J］.混凝土,2021(3):121-124.

[19] 何鹏涛,李新玲,沈卫国,等.模拟海水对高性能混凝土浆体的侵蚀作用研究［J］.硅酸盐通报,2016,35(10):3319-3323.

[20] 秦斌.海水海砂混凝土基本力学性能研究［J］.混凝土,2019(2):90-91.

[21] 韩刚,王学志,辛明,等.海水海砂混凝土力学性能研究综述［J］.辽宁工业大学学报(自然科学版),2021,41(6):405-408.

[22] 赵苏雅,吴庆,沈娇,等.海洋原材料制备的混凝土力学性能研究［J］.混凝土,2021(10):48-51+56.

[23] 姚武,吴梦雪,魏永起.三元复合胶凝体系中硅灰和粉煤灰反应程度的确定［J］.材料研究学报,2014,28(3):197-203.

张腾腾, 王传林, 张宇轩, 刘泽平. 粉煤灰掺量对海水海砂高性能混凝土性能的影响[J]. 硅酸盐通报, 2022, 41(5): 1677. ZHANG Tengteng, WANG Chuanlin, ZHANG Yuxuan, LIU Zeping. Effect of Fly Ash Content on Performance of High Performance Concrete with Seawater and Sea Sand[J]. Bulletin of the Chinese Ceramic Society, 2022, 41(5): 1677.

粉煤灰掺量对海水海砂高性能混凝土性能的影响

关于本站 Cookie 的使用提示

全站搜索

粉煤灰掺量对海水海砂高性能混凝土性能的影响

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索