TDDI产品Mo-Al-Mo膜层腐蚀原因分析及改善
[1] 刘翔, 陈旭, 谢振宇, 等.使用低电阻金属铝制造薄膜晶体管阵列信号电极[J].液晶与显示, 2009, 24(4): 533-536.
[2] HUANG J H, YEN S C. Electrochemical characteristics of molybdenumaluminum-neodymium double thin film in Tetramethyl-ammonium hydroxide solution [J]. Corrosion, 2007, 63(9): 835-842.
[3] 徐日庆, 邓祎文, 徐波, 等.基于SEM图像信息的软土三维孔隙率定量分析[J].地球科学与环境学报, 2015, 37(3): 104-110.
XU R Q, DENG Y W, XU B, et al. Quantitative analysis of soft clay three-dimensional porosity based on SEM image information [J]. Journal of Earth Sciences and Environment, 2015, 37(3): 104-110. (in Chinese)
[4] 陈兴伟, 吴建华, 王佳, 等.电偶腐蚀影响因素研究进展[J].腐蚀科学与防护技术, 2010, 22(4): 363-366.
CHEN X W, WU J H, WANG J, et al. Progress in research on factors influencing galvanic corrosion behavior [J]. Corrosion Science and Protection Technology, 2010, 22(4): 363-366. (in Chinese)
[5] 曹楚南.金属电化学腐蚀基本原理(上)[J].冶金建筑, 1981(5): 50-53.
CAO C N. Fundamentals of electrochemical corrosion of metal (1) [J]. Metallurgical Construction, 1981(5): 50-53. (in Chinese)
[6] 张文建, 吴明, 谢飞, 等.不同阴阳极面积比下X80钢在满洲里土壤中的腐蚀行为[J].材料保护, 2015, 48(5): 53-56, 9.
ZHANG W J, WU M, XIE F, et al. Corrosion behavior of X80 steel under different cathode /anode area ratio in simulated Manzhouli soil solution [J]. Materials Protection, 2015, 48(5): 53-56, 9. (in Chinese)
李森, 尚建兴, 张大伟, 田露, 张鹏曲, 肖红玺, 郝金刚, 黄东升, 王威, 张学智. TDDI产品Mo-Al-Mo膜层腐蚀原因分析及改善[J]. 液晶与显示, 2017, 32(11): 847. LI Sen, SHANG Jian-xing, ZHANG Da-wei, TIAN Lu, ZHANG Peng-qu, XIAO Hong-xi, HAO Jin-gang, HUANG Dong-sheng, WANG Wei, ZHANG Xue-zhi. Analysis and improvement of Mo-Al-Mo film corrosion in TDDI products[J]. Chinese Journal of Liquid Crystals and Displays, 2017, 32(11): 847.